Polycarbonate resin compositions

ABSTRACT

Polycarbonate resin compositions methods for their preparation are disclosed. The disclosed compositions are comprised of polycarbonate resins and α-olefin oligomers and exhibit good mold release and thermal stability while experiencing little discoloration or molecular weight reduction during molding.

The present invention relates to polycarbonate resin compositions, specifically to polycarbonate resin compositions having good mold release and thermal stability.

BACKGROUND OF THE INVENTION

Polycarbonates are usually manufactured by the phosgene process, but polycarbonates obtained in this way have the drawbacks of unsatisfactory thermal stability, and of poor mold release which complicates the continuous production of molded products from such polycarbonates.

Those problems are solved by the present invention, whose object is to provide polycarbonate resin compositions having good mold release and thermal stability.

SUMMARY OF THE INVENTION

The present invention consists of polycarbonate resin compositions containing

A) 100 wt. parts polycarbonates and

B) 0.001˜5 wt. parts α-olefin oligomers,

in which the polycarbonates are products of melt polymerization of aromatic dihydroxy compounds with carbonate diesters.

These polycarbonate resin compositions have extremely good mold release. They also show very little discoloration during molding. In addition, they have good thermal stability, so there is little fouling of molds in continuous production, and little lowering of melt viscosity during molding. These effects of the present invention are a dramatic improvement over those observed when polycarbonates made by the conventional phosgene process are used, or when common mold release agents are added.

These polycarbonate resin compositions are particularly suitable for use in optical applications, such as optical disks, lenses, optical fibers, lighting fixtures, etc.

The first essential condition of the present invention is the use of polycarbonates which are products of melt polymerization of aromatic dihydroxy compounds with carbonate diesters. As shown by the comparisons below, such an effect cannot be achieved when ordinary polycarbonates obtained by the phosgene process are used, even if α-olefin oligomers are added. On the other hand, using polycarbonates which are products of melt polymerization of aromatic dihydroxy compounds with carbonate diesters, in accordance with the present invention, the characteristics discussed above can be dramatically improved by the addition of α-olefin oligomers. This is something completely unforeseen.

The products of melt polymerization of aromatic dihydroxy compounds with carbonate diesters referred to here include all polycarbonates obtained by a melt process using aromatic dihydroxy compounds and carbonate diesters as the starting materials. The melt process itself is a known method of synthesizing polycarbonates by a transesterification reaction between dihydroxy compounds and carbonate diesters in their molten state.

There is no particular restriction on the aromatic dihydroxy compounds; any of the various types of known compounds can be used. Examples include, but are not limited to, compounds represented by the formula ##STR1## (where R^(a) and R^(b) are each independently a halogen or a monovalent hydrocarbyl group; X is --C(R^(c)) (R^(d))--, --C(═R^(e))--, --O--, --S--, --SO--, or --SO₂ --; R^(c) and R^(d) are each independently a hydrogen atom or a monovalent hydrocarbyl group; R^(e) is a divalent hydrocarbyl group; and p and q are each independently an integer 0˜4), such as bis(4-hydroxyphenyl)methane, 1,1-bis(4-hydroxyphenyl)ethane, 2,2-bis(4-hydroxyphenyl)propane, 2,2-bis(4-hydroxyphenyl)butane, 2,2-bis(4-hydroxyphenyl)octane, bis(4-hydroxyphenyl)phenylmethane, 2,2-bis(4-hydroxy-1-methylphenyl)propane, 1,1-bis(4-hydroxy-tert-butylphenyl)propane, 2,2-bis(4-hydroxy-3-bromophenyl)propane, and other bis(hydroxyaryl) alkanes; 1,1-bis(4-hydroxyphenyl)cyclopentane, 1,1-bis(4-hydroxyphenyl)cyclohexane, and other bis(hydroxyaryl)cycloalkanes; 4,4'-dihydroxydiphenyl ether, 4,4'-dihydroxy-3,3'-dimethylphenyl ether, and other dihydroxyaryl ethers; 4,4'-dihydroxydiphenyl sulfide, 4,4'-dihydroxy-3,3'-dimethylphenyl sulfide, and other dihydroxydiaryl sulfides; 4,4'-dihydroxydiphenyl sulfoxide, 4,4'-dihydroxy-3,3'-dimethyldiphenyl sulfoxide, and other dihydroxydiaryl sulfoxides; and 4,4'-dihydroxydiphenyl sulfone, 4,4'-dihydroxy-3,3'-dimethyldiphenyl sulfone, and other dihydroxydiaryl sulfones. Of these, 2,2-bis(4-hydroxyphenyl)propane is preferably used. Other aromatic dihydroxy compounds which can be used include compounds represented by the following general formula ##STR2## (where each R' is independently a hydrocarbyl group having 1-10 carbons, a halogenated hydrocarbyl group having 1-10 carbons, or a halogen atom, and m is an integer 0˜4), such as resorcin, 3-methylresorcin, 3-ethylresorcin, 3-propylresorcin, 3-butylresorcin, 3-tert-butylresorcin, 3-phenylresorcin, 3-cumylresorcin, 2,3-4,6-tertafluoresorcin, 2,3,4,6-tetrabromoresorcin, and other substituted resorcins; cathechol; hydroquinone, 3-methylhydroquinone, 3ethylhydroquinone, 3-propylhydroquinone, 3-butylhydroquinone, 3-tert-butylhydroquinone, 3-phenylhydroquinone, 3-cumylhydroquinone, 2,3,5,6-tetramethylhydroquinone, 2,3,5,6-tetra-tert-butylhydroquinone, 2,3,5,6-tetrafluorohydroquinone, 2,3,5,6-tetrabromohydroquinone, and other substituted hydroquinones; as well as 2,2,2', 2'-tetrahydro-3,3,3', -3'-tetramethyl-1,1'-spirobi-[1H-indene]-7,7'-diol represented by the following formula. ##STR3##

These aromatic dihydroxy compounds may be used singly or in combinations of two or more.

There is no particular restriction on the carbonate diesters, either. Examples include, but are not limited to, diphenyl carbonate, ditolyl carbonate, bis(chlorophenyl) carbonate, m-cresyl carbonate, dinaphthyl carbonate, bis(diphenyl) carbonate, diethyl carbonate, dimethyl carbonate, dibutyl carbonate, dicyclohexyl carbonate, etc. Diphenyl carbonate is preferably used.

These carbonate esters may be used singly or in combinations of two or more.

These carbonate diesters may also contain dicarboxylic acids or dicarboxylate esters. Examples of dicarboxylic acids and dicarboxylate esters include aromatic dicarboxylic acids and their derivatives, such as terephthalic acid, isophthalic acid, diphenyl terephthalate, diphenyl isophthalate, etc.; aliphatic dicarboxylic acids and their derivatives, such as succinic acid, glutaric acid, adipic acid, pimelic acid, suberic acid, azelaic acid, sebacic acid, decanedioic acid, dodecanedioic acid, diphenyl sebacate, diphenyl decanedioate, diphenyl dodecanedioate, etc.; and alicyclic dicarboxylic acids and their derivatives, such as cyclopropanedicarboxylic acid, 1,2-cyclobutanedicarboxylic acid, 1,3-cyclobutanedicarboxylic acid, 1,2-cyclopentanedicarboxylic acid, 1,3-cyclopentanedicarboxylic acid, 1,2-cyclohexanedicarboxylic acid, 1,3-cyclohexanedicarboxylic acid, 1,4-cyclohexanedicarboxylic acid, diphenyl cyclopropanedicarboxylic, diphenyl 1,2-cyclobutanedicarboxylate, diphenyl 1,3-cyclobutanedicarboxylate, diphenyl 1,2-cyclopentandedicarboxylate, diphenyl 1,3-cyclopentanedicarboxylate, diphenyl 1,2-cyclohexanedicarboxylate, diphenyl 1,3-cyclohexanedicarboxylate, diphenyl 1,4-cyclohexanedicarboxylate, etc. These dicarboxylic acids and dicarboxylate esters may be used singly or in combinations of two or more. The carbonate diesters preferably contain no more than 50 mole % more preferably no more than 30 mole %, such dicarboxylic acids and dicarboxylate esters.

In the manufacture of the polycarbonates, in addition to the aromatic dihydroxy compounds and carbonate diesters, one can also use polyfunctional compounds having three or more functional groups per molecule. Such polyfunctional compounds are preferably compounds having phenolic hydroxy groups or carboxy groups; those having 3 phenolic hydroxy groups are particularly preferred. Examples of such preferred compounds include 1,1,1-tris(4-hydroxyphenyl)ethane, 2,2',2"-tris(4-hydroxyphenyl)diisopropylbenzene [sic], α-methyl-α, α', α'-tris(4-hydroxyphenyl)-1,4-diethylbenzene, α,α', α"-tris-(4-hydroxypenyl)-1,3,5-triisopropylbenzene, phloroglucin, 4,6-dimethyl-2,4,6-tri(4-hydroxyphenyl)heptane-2,1,3,5-tri(4-hydroxyphenyl)benzene. 2,2-bis[4,4-(4,4'-dihydroxyphenyl)cyclohexyl]propane, trimellitic acid, 1,3,5-benzenetricarboxylic acid, pyromellitic acid, etc. Particularly preferred are 1,1,1-tris(4-hydroxyphenyl)ethane, α,α',α"-tris(4-hydroxyphenyl)-1,3,5-triisoopropylbenzene, etc. The polyfunctional compounds are preferably used in amounts of up to 0.03 mole, more preferably 0.001˜0.02 mole, most preferably 0.001˜0.01 mole, per mole of aromatic dihydroxy compounds.

Compounds which form one or more terminal groups represented by the formula ##STR4## (where the aromatic ring or the chromanyl group may be substituted with halogens or alkyl groups having 1-9 carbons) can also be used in the manufacture of polycarbonates. Compounds capable of introducing hydroxy groups (1) include diols such as bisphenol A. Compounds capable of introducing phenoxy groups (2) include phenol, diphenyl carbonate, etc. Compounds capable of introducing p-tert-butylphenoxy groups (3) include p-tert-butylphenol, p-tert-butylphenol phenyl carbonate, p-tert-butylphenyl carbonate, etc. Compounds capable of introducing p-cumylphenoxy groups (p-phenylisopropylphenoxy groups) (4) include p-cumylphenol, p-cumylphenyl phenyl carbonate, p-cumylphenyl carbonate, etc. Chromanylphenoxy groups (5) of the type indicated in the formula include those having the following formulas. ##STR5## Compounds capable of introducing groups represented by (5-1) include 2,2,4-trimethyl-4-(4-hydroxyphenyl)chroman, 2,2,4,6-tetramethyl-4-(3,5-dimethyl-4-hydroxyphenyl)chroman, 2,3,4-trimethyl-2-ethyl-4-(3-nonyl-4-hydroxyphenyl)-7-nonylchroman, 2,2,4-trimethyl-4-(3,5-diethyl-4-hydroxyphenyl)-6-ethylchroman, 2,2,4,6,8-pentamethyl-4-(3,5-dimethyl-4-hydroxyphenyl)chroman, 2,2,4-triethyl-3-methyl-4-(4-hydroxyphenyl)chroman, 2,2,4-trimethyl-4-(3-bromo-4-hydroxyphenyl)-6-bromochroman, 2,2,4-trimethyl-4-(3,5-dibromo-4-hydroxyphenyl)-6-bromochroman, 2,2,4-trimethyl-4-(3,5-dibromo-4-hydroxyphenyl)-6,8-dibromochroman, etc. Of these, 2,2,4-trimethyl-4-(4-hydroxyphenyl)chroman is particularly preferred. Compounds capable of introducing groups represented by (5-2) include 2,2,3-trimethyl-3-(4-hydroxyphenyl)chroman, 2,2,3,6-tetramethyl-3-(3,5-dimethyl-4-hydroxyphenyl)chroman, 2,3,4-trimethyl-2-ethyl-3-(3-nonyl-4-hydroxyphenyl)-7-nonylchroman, 2,2,3-trimethyl-3-(3,5-diethyl-4-hydroxyphenyl)-6-ethylchroman. 2,2,3-6,8-pentamethyl-3-(3,5-dimethyl-4-hydroxyphenyl)chroman, 2,2,3-triethyl-3-methyl-3(4-hydroxyphenyl)chroman, 2,2,3-trimethyl-3-(3-bromo-4 -hydroxyphenyl)-6-bromochroman, 2,2,3-trimethyl-3-(3,5-dibromo-4-hydroxyphenyl)-6-bromochroman, 2,2,3-trimethyl-3-(3,5-dibromo-4-hydroxyphenyl)-6,8-dibromochroman, etc. Of these, 2,2,3-trimethyl-3-(4-hydroxyphenyl)chroman is particularly preferred. Compounds capable of introducing groups represented by (5-3) include 2,4,4-trimethyl-2-(2-hydroxyphenyl)chroman. 2,4,4,6-tetramethyl-2-(3,5-dimethyl-2-hydroxyphenyl)chroman, 2,3,4-trimethyl-4-ethyl-2-(3,5-dimethyl-2-hydroxyphenyl)-7-nonylchroman, 2,4,4-trimethyl-2-(3,5-dimethyl-2-hydroxyphenyl)-6-ethylchroman, 2,4,4,6,8-pentamethyl-2-(3,5-dimethyl-2-hydroxyphenyl)-6-ethylchroman, 2,4,4-trimethyl-2-(3-bromo-2-hydroxyphenyl)chroman, 2,4,4-trimethyl-2-(3-bromo-2-hydroxyphenyl)-6-bromochroman, 2,4,4-trimethyl-2-(3,5-dibromo-2-hydroxyphenyl)-6-bromochroman, 2,4,4-trimethyl-2-(3,5-dibromo-2-hydroxyphenyl)-6,8-dibromochroman, etc. Of these, 2,2,4-trimethyl-2-(2-hydroxyphenyl)chroman [sic] is particularly preferred. Compounds capable of introducing groups represented by (5-4) include 2,4,4-trimethyl-2-(4-hydroxyphenyl)chroman, 2,4,4,6-tetramethyl-2-(3,5-dimethyl-4-hydroxyphenyl)chroman, 2,4,4-triethyl-2-(4-hydroxyphenyl)chroman, 2,3,4-trimethyl-4-ethyl-2-(3,5-dimethyl-4-hydroxyphenyl)-7-nonylchroman, 2,4,4-trimethyl-2-(3,5-diethyl-4-hydroxyphenyl)-6-ethylchroman, 2,4,4,6,8-pentamethyl-2-(3,5-dimethyl-4-hydroxyphenyl)-6-ethylchroman, 2,4,4-trimethyl-2-(3-bromo-4-hydroxyphenyl)chroman, 2,4,4-trimethyl-2-(3-bromo-4-hydroxyphenyl)-6-bromochroman, 2,4,4-trimethyl-2-(3,5-dibromo-4-hydroxyphenyl)-6-bromochroman, 2,4,4-trimethyl-2-(3,5-dibromo-4-hydroxyphenyl)-6,8-dibromochroman, etc. Of these, 2,4,4-trimethyl-2-(4-hydroxyphenyl)chroman is particularly preferred. All of these compounds may also have halogen or C₁₋₉ alkyl substituent groups on the aromatic or the aliphatic rings. These compounds may be used singly or in combinations of 2 or more. In the present invention, the residues of these dihydroxy compounds are preferably no more than 50%, most preferably no more than 30%, of the total terminal groups.

The amount of carbonate diesters used should be 1.00˜1.30 moles, most preferably 1.01˜1.20 moles, per mole of aromatic dihydroxy compounds. The monomers should be made to react in the presence of a catalyst.

The catalyst used may be, for example, one of the compounds proposed by the present applicants in the specification of Japanese Patent Application No. 2-85218. Preferred examples include (a) organic acid salts, inorganic acid salts, oxides, hydroxides, hydrides, or alcoholates of metals such as alkali metals or alkaline-earth metals. Specific examples of such compounds include, but are not limited to, sodium hydroxide, potassium hydroxide, lithium hydroxide, sodium hydrogen carbonate, potassium hydrogen carbonate, lithium hydrogen carbonate, sodium carbonate, potassium carbonate, lithium carbonate, sodium acetate, potassium acetate, lithium acetate, sodium stearate, potassium stearate, lithium stearate, sodium boron hydroxide, lithium boron hydroxide, sodium phenyl borate, sodium benzoate, potassium benzoate, lithium benzoate, disodium hydrogen phosphate, dipotassium hydrogen phosphate, dilithium hydrogen phosphate, the disodium or dipotassium or dilithium salt of bisphenol A, the sodium or potassium or lithium salt of phenol, etc.; calcium hydroxide, barium hydroxide, magnesium hydroxide, strontium hydroxide, calcium hydrogen carbonate, barium hydrogen carbonate, magnesium hydrogen carbonate, strontium hydrogen carbonate, calcium carbonate, barium carbonate, magnesium carbonate, strontium carbonate, calcium acetate, barium acetate, magnesium acetate, strontium acetate, calcium stearate, barium stearate, magnesium stearate, strontium stearate, etc. These compounds may be used singly or in combinations of two or more. The amount of such alkali metal compounds and/or alkaline-earth metal compounds used is preferably 10⁻⁸ ˜10⁻³ mole, more preferably 10⁻ 7 ˜10⁻⁶ mole, most preferably 10⁻⁷ ˜8×10⁻⁷ mole, per mole of aromatic dihydroxy compounds.

In addition to these alkali metal compounds and/or alkaline-earth metal compounds, basic compounds (b) may also be used as catalysts. Examples of basic compounds include, but are not limited to, nitrogen compounds such as substituted ammonium hydroxides having alkyl, aryl, or alkaryl groups, e.g., tetramethylammonium hydroxide, tetraethylammonium hydroxide, tetrabutylammonium hydroxide, trimethylbenzylammonium hydroxide, etc.; tertiary amines such as trimethylamine, triethylamine, dimethylbenzylamine, triphenylamine, etc.; secondary or primary amines having methyl, ethyl, or other alkyl groups or phenyl, tolyl, or other aryl groups; ammonia; and basic salts such as tetramethylammonium borohydride, tetrabutylammonium borohydride, tetrabutylammonium tetraphenylborate, tetramethylammonium tetraphenylborate, etc. Of these, the ammonium hydroxides are particularly preferred. These basic compounds may be used singly or in combinations of two or more.

In the present invention, by using a combination of the above-mentioned

(a) alkali metal compounds and/or alkaline-earth metal compounds, and

(b) nitrogen-containing basic compounds,

it is possible to obtain high-molecular-weight polycarbonates with high polymerization activity.

It is also possible to use a combination of

(a) alkali metal compounds and/or alkaline-earth metal compounds,

(b) nitrogen-containing basic compounds, and

(c) boric acid and/or borate esters.

When this type of combination is used as the catalyst, the (a) alkali metal compounds and/or alkaline-earth metal compounds are preferably used in the amounts specified above, and the (b) nitrogen-containing basic compounds are preferably used in amounts of 10⁻⁶ ˜10⁻¹ mole, most preferably 10⁻⁵ ˜10⁻² mole, per mole of aromatic dihydroxy compounds. The (c) boric acid or borate esters are preferably compounds represented by the following general formula

    B(OR.sup.g).sub.r (OH).sub.3-r

(where R^(g) is a hydrogen atom, an aliphatic hydrocarbyl group, an alicyclic hydrocarbyl group, or an aromatic hydrocarbyl group, and r is an integer 1˜3). Examples include boric acid, trimethyl borate, triethyl borate, tributyl borate, trihexyl borate, triheptyl borate, triphenyl borate, tritolyl borate, trinaphthyl borate, etc. Of these, triphenyl borate is particularly preferred. The amount of (c) boric acid or borate ester used as a catalyst along with the above-mentioned compounds (a) and (b) is preferably 10⁻⁶ ˜10⁻¹ mole, most preferably 10⁻⁵ ˜10⁻² mole, per mole of aromatic dihydroxy compounds.

There is no restriction on conditions such as temperature and pressure during the melt polymerization reaction. The usual conditions for known processes can be used. The first-stage reaction is preferably carried out at 80°˜250° C., more preferably 100°˜230° C., most preferably 120°˜190° C., preferably for a period of 0˜5 hours, more preferably 0˜4 hours, most preferably 0.25˜3 hours, at ambient pressure. Then the reaction between the aromatic dihydroxy compounds and the carbonate diesters proceeds as the pressure in the reaction system is reduced and the temperature increased, and finally the reaction between aromatic dihydroxy compounds and carbonate diesters is completed in vacuo, preferably at 0.05˜5 mm Hg and 240°˜320° C.

The reaction between the types of aromatic dihydroxy compounds and carbonate diesters described above may be carried out continuously or batchwise. The apparatus used for this reaction may be a tank, a tubular reactor, or a reaction column.

Polycarbonates of this sort should preferably have an intrinsic viscosity, measured at 20° C. in methylene chloride, of 0.30˜0.65 dL/g, most preferably 0.32˜0.62 dL/g, especially if the resin composition is to be used for optical applications. If the intrinsic viscosity is too high, the melt flow of the material will be lowered, making it necessary to mold it at temperatures in excess of 400° C. At such temperatures it would be impossible to avoid decomposition of the resin, which could cause silver streaks or otherwise impair the transparency of the molded products. If the intrinsic viscosity is too low, there may be impairment of properties such as strength and heat resistance, and molding problems such as a tendency to crystallize easily.

The second essential condition in the present invention is that the resin composition contain 0.001˜5 wt. parts α-olefin oligomers per 100 wt. parts polycarbonates.

There is no particular restriction on the α-olefin oligomers; all oligomers made up of α-olefin units are included. Nor is their any restriction on the α-olefin itself. Examples, such as those listed in Japanese Early Patent Disclosure Publication No. 62-190250, include n-α-olefins having 6 to 12 carbons, of which 1-undecene is a representative example. The α-olefin oligomers are preferably chains of 2˜7 repeating units, or mixtures thereof. It is also desirable that the oligomers be hydrogenated to eliminate any unsaturated bonds. Particularly preferred are 1-undecene dimers, trimers, tetramers, pentamers, or mixtures thereof, Examples include 9-methyl-11-n-octylheneicosane, and Emery 3002®, Emery 3004®, and Emery 3006® manufactured by Emery Industries.

Resin compositions in accordance with the present invention also preferably contain 0.1˜10 ppm, most preferably 0.5˜5 ppm, of acidic sulfur-containing compounds having a pK, of 3 or below, or derivatives of such compounds. They make the polycarbonate resin compositions more heat resistant, in particular by inhibiting molecular weight reduction during molding. Any such compound having a pK_(a) of 3 or below, or derivative thereof, may be used. Preferred compounds include those represented by the following formula ##STR6## (where R¹ is an alkyl group having 1˜50 carbons, in which halogen atoms may be substituted for hydrogen atoms; R² is a hydrogen atom or an alkyl group having 1˜50 carbons, in which halogen atoms may be substituted for hydrogen atoms; and n is an integer 0˜3). Specific examples of such compounds include, but are not limited to, sulfonic acids such as benzenesulfonic acid and ρ-toluenesulfonic acid; sulfonic acid esters such as methyl benzenesulfonate, ethyl benzenesulfonate, butyl benzenesulfonate, octyl benzenesulfonate, phenyl benzenesulfonate, methyl ρ-toluenesulfonate, ethyl ρ-toluenesulfonate, butyl ρ-toluenesulfonate, octyl ρ-toluenesulfonate, and phenyl ρ-toluenesulfonate; and compounds such as trifluoromethanesulfonic acid, naphthalenesulfonate acid, sulfonated polystyrene, methyl acrylate-sulfonated styrene copolymer, etc. It is also possible to use two or more of these compounds together. Butyl ρ-toluenesulfonate is particularly preferred.

Polycarbonate resin compositions in accordance with the present invention may also contain added boron compounds. The boron compounds may be boric acid or borate esters such as those listed previously as catalyst components. Adding such boron compounds can prevent discoloration of the polycarbonate resin composition during molding. The amount of boron compounds added is preferably 0.00001˜0.2 wt. part, most preferably 0.00005˜0.02 wt. part, per 100 wt. parts of polycarbonate. If boron compounds are added as catalyst components during polymerization of the polycarbonate, there is no need to add more after polymerization.

However, if the amount of such boron compounds or acidic sulfur compounds or derivatives used is excessive, the water resistance of the polycarbonate resin composition may be lowered.

Polycarbonate resin compositions in accordance with the present invention may also contain phosphorus compounds or carboxylate esters added as processing stabilizers (antioxidants). Among the phosphorus compounds which may be used are phosphate esters and phosphite esters. Examples of phosphate esters include trialkyl phosphates such as trimethyl phosphate, triethyl phosphate, tributyl phosphate, trioctyl phosphate, tridecyl phosphate, trioctadecyl phosphate, distearyl pentaerythrityl diphosphate, tris(2-chloroethyl) phosphate, and tris(2,3-dichloropropyl) phosphate; tricycloalkyl phosphates such as tricyclohexyl phosphate; and triaryl phosphates such as triphenyl phosphate, tricresyl phosphate, tris(nonylphenyl) phosphate, and 2-ethylphenyl diphenyl phosphate. Examples of phosphite esters include trialkyl phosphites such as trimethyl phosphite, triethyl phosphite, tributyl phosphite, trioctyl phosphite, tris(2-ethylhexyl) phosphite, trinonyl phosphite, tridecyl phosphite, trioctadecyl phosphite, tristearyl phosphite, tris(2-chloroethyl) phosphite, and tris(2,3-dichloropropyl) phosphite; tricycloalkyl phosphites such as tricyclohexyl phosphite; triaryl phosphites such as triphenyl phosphite, tricresyl phosphite, tris(ethylphenyl) phosphite, tris(2,4-di-tert-butylphenyl) phosphite, tris(nonylphenyl) phosphite, and tris(hydroxyphenyl) phosphite; aryl alkyl phosphites such as phenyl didecyl phosphite, diphenyl decyl phosphite, diphenyl isooctyl phosphite, phenyl isooctyl phosphite, and 2-ethylhexyl diphenyl phosphite; as well as distearyl pentaerythrityl diphosphite, bis(2,4-di-tert-butylphenyl)pentaerythrityl diphosphite, and phosphite esters represented by the general formula

    P(OR.sup.h).sub.3

(where each R^(h) is independently an aliphatic hydrocarbyl group, alicyclic hydrocarbyl group, or aromatic hydrocarbyl group). One can also use hypophosphorous acid, pyrophosphoric acid, polyphosphoric acid, etc. Of these various compounds, phosphite esters are preferred, especially tris(2,4-di-tert-butylphenyl) phosphite. Examples of carboxylate esters, in addition to the compounds previously listed, include but are not limited to n-octadecyl 3-(4'-hydroxy-3',5'-di-tert-butylphenyl)propionate, various alicyclic diepoxy carboxylates, etc. Two or more stabilizers may be used together. These compounds are preferably used in amounts not exceeding 0.1 wt. part per 100 wt. parts of polycarbonate.

Polycarbonate resin compositions in accordance with the present invention also preferably contain epoxy compounds, so that excess boron compounds or acidic sulfur compounds present in the resin composition will react with the epoxy compounds and be neutralized, making it possible to form moldings having excellent color tone, heat resistance, water resistance, etc. The epoxy compounds used may be any compounds having one or more epoxy groups per molecule. Examples include, but are not limited to, epoxidized soybean oil, epoxidized linseed oil, phenyl glycidyl ether, allyl glycidyl ether, tert-butylphenyl glycidyl ether, 3,4-epoxycyclohexylmethyl 3,4-epoxycyclohexanecarboxylate, 3,4-epoxy-6-methylcyclohexylmethyl 3,4-epoxy-6-methylcyclohexanecarboxylate, 2,3-epoxycyclohexylmethyl 3,4-epoxycyclohexanecarboxylate, 4-(3,4-epoxy-5-methylcyclohexyl)butyl 3,4-epoxycyclohexanecarboxylate, 3,4-epoxycyclohexylethylene oxide, cyclohexylmethyl 3,4-epoxycyclohexanecarboxylate, 3,4-epoxy-6-methylcyclohexylmethyl 6-methylcyclohexanecarboxylate, bisphenol A diglycidyl ether, tetrabromobisphenol A glycidyl ether, the diglycidyl ester of phthalic acid, the diglycidyl ester of hexahydrophthalic acid, bis(epoxydicyclopentadienyl) ether, bis-epoxyethylene glycol [sic], bis(epoxycyclohexyl) adipate, butadiene diepoxide, tetraphenylethylene epoxide, octyl epoxy talate [sic], epoxidized polybutadiene, 3,4-dimethyl-1,2-epoxycyclohexane, 3,5-dimethyl-1,2-epoxycyclohexane, 3-methyl-5-tert-butyl-1,2-epoxycyclohexane, octadecyl 2,2-dimethyl-3,4-epoxycyclohexanecarboxylate, n-butyl 2,2-dimethyl-3,4-epoxycyclohexanecarboxylate, cyclohexyl 2-methyl-3,4-epoxycyclohexanecarboxylate, n-butyl 2-isopropyl-3,4-epoxy-5-methylcyclohexanecarboxylate, octadecyl 3,4-epoxycyclohexanecarboxylate, 2-ethylhexyl 3',4'-epoxycyclohexanecarboxylate, 4,6-dimethyl 2,3-epoxycyclohexyl 3',4'-epoxycyclohexanecarboxylate, 4,5-epoxytetrahydrophthalic anhydride, 3-tert-butyl-4,5-epoxytetrahydrophthalic anhydride, diethyl 4,5-epoxy-cis-1,2-cyclohexanedicarboxylate, di-n-butyl 3-tert-butyl-4,5-epoxy-cis-1,2-cyclohexanedicarboxylate, etc. These epoxy compounds may be used singly, or in combinations of two or more. There is a particular limitation on the amount of epoxy compound used, but it is usually preferable to add 0.001˜ 0.1 wt. part, most preferably 0.001˜0.08 wt. part, per 100 wt. parts of polycarbonates.

Polycarbonate resin compositions in accordance with the present invention may also contain one or more common additives such as heat stabilizers, weather stabilizers, antistatic agents, slip agents, antiblocking agents, antifogging agents, lubricants, dyes, pigments, natural oils, synthetic oils, waxes, organic fillers, inorganic fillers, etc., in amounts which do not interfere with the object of the present invention.

There is no particular restriction on the method used to combine these components to form resin compositions in accordance with the present invention. The components may be mixed in any order. For example, the α-olefin oligomers and any optional components may be added to the molten polycarbonate and kneaded, or the α-olefin oligomers and any optional components may be added to a solution of the polycarbonate and later kneaded. More specifically, the molten polycarbonate reaction product obtained on completion of polymerization may be mixed in the reaction vessel or extruder with the α-olefin oligomers and any optional components, either one after another or all at once. Or the polycarbonate may be pelletized first, and the pellets then fed to a single-screw or twin-screw extruder along with the α-olefin oligomers and any optional components, and melt kneaded. It is also possible to dissolve the polycarbonate in a suitable solvent (e.g., methylene chloride, chloroform, toluene, tetrahydrofuran, etc.), then add the α-olefin oligomers and any optional components to the solution, either one after another or all at once, while stirring.

Polycarbonate resin compositions in accordance with the present invention are preferably subjected to a vacuum treatment. There is no particular restriction on the process or equipment used for vacuum treatment. For example, one could use a reactor having a vacuum device, or a vacuum-vented extruder. The reactor having a vacuum pumping device may be either a vertical tank reactor or a horizontal tank reactor, although horizontal tank reactors are preferred. The vacuum-vented extruder may be either a single-screw or a twin-screw extruder, which carries out the vacuum treatment while pelletizing the polymer. If the vacuum treatment is performed in an evacuated reactor vessel, the pressure is preferably lowered to 0.05˜750 mm Hg, most preferably 0.05˜5 mm Hg. If the vacuum treatment is performed in an extruder, the pressure is preferably lowered to 1˜750 mm Hg, most preferably 5˜700 mm Hg. This kind of vacuum treatment is preferably performed at 240°˜350° C., for a period of 5 minutes to 3 hours in a reactor, or 10 seconds to 15 minutes in an extruder. Performing such a vacuum treatment makes it possible to obtain polycarbonate compositions containing less residual monomers or oligomers. For example, in the case of melt polymerization using diphenyl carbonate as the carbonate diester, vacuum treatment can decrease the amount of residual diphenyl carbonate in the polycarbonate. The polycarbonate should preferably contain no more than 0.1 wt. part, most preferably no more than 0.01 wt. part, of residual diphenyl carbonate.

Resin compositions thus obtained, in accordance with the present invention, show good mold release and thermal stability, with very little discoloration or mold fouling when they are molded.

The present invention will now be described in greater detail by means of some examples, although it is by no means limited to these examples.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS REFERENCE EXAMPLE 1 Synthesis of Polycarbonate (PC1) by Melt Process

A 250-liter stirred tank reactor was filled with 0.44 kilomole of bisphenol A (from Nihon GE Plastics) and 0.44 kilomole of diphenyl carbonate (from Eni Co.), then purged with nitrogen, and the contents were melted at 140° C.

The temperature was raised to 180° C., 0.011 mole of triphenyl borate was added, and the mixture was stirred for 30 minutes.

Then 0.00044 mole of sodium hydroxide and 0.11 mole of tetramethylammonium hydroxide were added, and stirring was continued for 30 minutes, after which the temperature was raised to 210° C. as the pressure was gradually lowered to 200 mm Hg. After 30 minutes, the temperature was increased to 240° C. and the pressure gradually lowered to 15 mm Hg. The temperature and pressure were then kept constant, and the amount of phenol distilled off was measured. When phenol stopped distilling off, the reactor was filled with nitrogen to restore it to atmospheric pressure. The time required for the reaction was 1 hour.

The intrinsic viscosity (η) of the reaction product was 0.15 dL/g.

The reaction product was then fed by a gear pump to a centrifugal thin-film evaporator for further reaction. The evaporator temperature and pressure were controlled at 270° C. and 2 mm Hg. A gear pump was used to feed the product from the bottom of the evaporator at a rate of 40 kg/hr to a horizontal twin-impeller stirred tank (L/D=3, impeller blade diameter 220 mm, capacity 80 liters), where polymerization was continued at 290° C. and 0.2 mm Hg, with a residence time of 30 minutes.

The molten polymer was then fed by a gear pump to a twin-screw extruder (L/D=17.5, barrel temperature 285° C.), to which 2 ppm of butyl ρ-toluenesulfonate was added and kneaded into the polymer. The resulting polymer was extruded through a die to form a strand, and cut into pellets.

The intrinsic viscosity (IV) of the polymer thus obtained was 0.49 dL/g.

REFERENCE EXAMPLE 2 Synthesis of Lower-Viscosity Polycarbonate (PC3) by Melt Process

A reaction product obtained as in the first part of Reference Example 1, having intrinsic viscosity (η) 0.15 dL/g, was fed by a gear pump to a centrifugal thin-film evaporator for further reaction. The evaporator temperature and pressure were controlled at 270° C. and 2 mm Hg. A gear pump was used to feed the product from the bottom of the evaporator at a rate of 40 kg/hr to a horizontal stirred tank with twin impellers (L/D=3, impeller blade diameter 220 mm, capacity 80 liters) where polymerization was continued at 280° C. and 0.2 mm Hg, with a residence time of 30 minutes.

The molten polymer was then fed by a gear pump to a twin-screw extruder (L/D=17.5, barrel temperature 285° C.), to which 2 ppm of butyl p-toluenesulfonate was added and kneaded into the polymer, which was extruded through a die to form a strand, and cut into pellets.

The intrinsic viscosity (IV) of the polymer thus obtained was 0.345 dL/g.

EXAMPLES 1˜3, COMPARISONS 1˜4

The following components were combined in the proportions shown in Table 1, mixed in a single-screw extruder (L/D=17.5, temperature 280° C.), and pelletized.

PC1: polycarbonate obtained in Reference Example 1

PC2: polycarbonate made from bisphenol A by phosgene process (intrinsic viscosity 0.50 dL/g)

Emery 3002®: α-olefin oligomer (average of 20 carbons per molecule) comprising 1-undecene dimer, from Emery Industries

Emery 3004®: α-olefin oligomer (average of 31 carbons per molecule), 89% 1-undecene trimer and 11% 1-undecene tetramer, from Emery Industries

Emery 3006®: α-olefin oligmer (average of 31 carbons per molecule), 29% 1-undecene trimer, 62% 1-undecene tetramer, and 9% 1-undecene pentamer, from Emery Industries

TSF437®: silicone oil, from Toshiba Silicone

Stabilizers:

Stb1: tris(2,4-di-tert-butylphenyl) phosphite [MK 2112E®, from Adeka Argus]

Stb2: n-octadecyl 3-(4'-hydroxy-3'-5'-di-tert-butylphenyl)propionate

Stb3: alicyclic diepoxy carboxylate [Celloxide 2021P®, from Daicel]

The resulting pellets were fed to a single-screw extruder (L/D=28, temperature 280° C.), then to a 150-t injection-molding machine (cylinder temperature 280° C., mold temperature 80° C.) to form moldings (150 mm high, 80 mm wide, 70 mm thick).

The moldings thus obtained were evaluated as follows.

Ejector Pin Force (kg_(f)) (mean, n=10): The force applied by the ejector pin, measured during ejection of the moldings

Deformation by Ejector Pin: Each molding was examined visually for deformation at the point where the ejector pin struck it.

Mold Fouling (after 10,000 shots): The polished surfaces of the mold were examined visually for fouling after continuous molding of 3-mm plates (cylinder temperature 290° C., injection pressure 1000 kg/cm², cycle time 45 sec, mold temperature 90° C.) for 10,000 shots

Initial YI (Yellowness Index): The X, Y, and Z values of the 3-mm plates (molded at cylinder temperature 290° C., injection pressure 1000 kg/cm², cycle time 45 sec, mold temperature 90° C.) were measured by the transmission method using an ND-1001 DP Color and Color Difference Meter (from Nippon Denshoku Kogyo), and the yellowness index was calculated using the formula YI=100×(1.277 X-1.060 Z)/Y

YI After 15 Minutes at 320° C. ("320-15 YI" in Table 1): Injection moldings were prepared as above, except that the cylinder temperature was 320° C. and the composition was held in the cylinder for 15 minutes before injection, then the YI of the moldings was determined as above.

Initial MI (melt index): The melt index of the pelletized composition was measured by the JIS K-7210 standard method, at 300° C. with a load of 1.2 kg.

MI After 15 Minutes at 320° C. ("320-15 MI" in Table 1): Measured as for the initial MI, using plates molded after holding up the resin for 15 minutes at 320° C. as described above

The results are shown in Table 1.

                  TABLE 1                                                          ______________________________________                                                Experiment*                                                                                       Co.  Co.   Co.                                              Ex. 1                                                                               Ex. 2  Ex. 3  1    2     3     Co. 1                               ______________________________________                                         Composition                                                                    PC1      100    100    100  --   --    100   100                               PC2      --     --     --   100  100   --    --                                Emery 3004                                                                              0.15   0.3    0.6  0.3  0.6   --    --                                TSF437   --     --     --   --   --    --    0.3                               Stb1     0.03   0.03   0.03 0.03 0.03  0.03  0.03                              Stb2     0.03   0.03   0.03 0.03 0.03  0.03  0.03                              Stb3     0.03   0.03   0.03 0.03 0.03  0.03  0.03                              Characteristic                                                                 Ejector Pin                                                                             670    618    420  625  415   980   878                               Force                                                                          Deformation                                                                             none   none   none none none  much  much                              by Ejector                                                                     Pin                                                                            Mold Fouling                                                                            none   none   none some very  none  none                              After 10,000                     much                                          Shots                                                                          Initial YI                                                                               1.8    1.8    1.9  1.8  1.9   1.7   1.8                              320-15 YI                                                                                1.8    1.9    2.1  2.2  2.4   1.7   1.8                              Initial MI                                                                              10.8   11.0   11.0 10.5 10.9  10.4  10.7                              320-15 MI                                                                               11.2   11.8   11.8 13.6 14.0  11.0  11.6                              ______________________________________                                          *Ex.→ Example, Co.→ Comparison                             

EXAMPLES 4˜5, COMPARISONS 5˜7

The following components were combined in the proportions shown in Table 2, and used to mold compact disks (CDs) 120 mm in diameter using a nickel stamper, with a cylinder temperature of 350° C., a cycle time of 7 seconds, and a mold temperature of 80° C., in a continuous operation for 24 hours.

PC3: polycarbonate obtained in Reference Example 2

PC4: polycarbonate made from bisphenol A by phosgene process

Emery 3004

Stb1

Stb3

The resulting CDs were tested for the following characteristics.

Continuous Production Quality: Noted whether problems occurred during the continuous production run

Stamper Fouling at 24 hours: After producing CDs continuously as described above for 24 hours, the stamper was examined visually for fouling

The results are shown in Table 2.

                  TABLE 2                                                          ______________________________________                                                      Experiment.sup.1)                                                              Ex. 4                                                                               Ex. 5  Co. 5   Co. 6 Co. 7                                   ______________________________________                                         PC3            100    100    --    --    100                                   PC4            --     --     100   100   --                                    Emery 3004     0.1    0.3    0.1   0.3   --                                    Stb1           0.01   0.01   0.01  0.01  0.01                                  Stb3           0.01   0.01   0.01  0.01  0.01                                  Characteristic                                                                 Suitability for                                                                               OK     OK     OK    OK    NG.sup.2)                             Continuous Production                                                          Stamper Fouling                                                                               none   none   some  much  --                                    After 24 Hours                                                                 ______________________________________                                          .sup.1) Ex.→ Example, Co.→ Comparison                            .sup.2) Continouous production impossible due to problems caused by poor       mold release (disk sticking in mold, etc.)                               

As can be seen from the examples, resin compositions in accordance with the present invention show better mold release and thermal stability, and consequently less mold fouling and better continuous production characteristics, than compositions having as their main component polycarbonate resins obtained by the phosgene process. Resin compositions in accordance with the present invention also have the advantage of showing very little discoloration during molding. 

What is claimed is:
 1. A polycarbonate resin composition comprising(A) 100 parts by weight of a polycarbonate having a viscosity-average molecular weight of about 12,000-18,000 (B) 0.001-5 parts by weight of an α-olefin oligomer and (C) 0.00001-0.00045 parts by weight of an acidic sulfur-containing compound having a pKa of no more than 3 or a derivative formed from such a compound wherein the polycarbonate is a product of melt polymerization of an aromatic dihydroxy compound and a carbonate diester.
 2. The polycarbonate resin composition of claim 1, in which the α-olefin oligomer contains a compound selected from the group consisting of 1-undecene dimer, trimer, tetramer, and pentamer.
 3. The polycarbonate resin composition of claim 1 wherein the sulfur-containing compound is represented by the formula ##STR7## where R¹ is an alkyl group having 1-50 carbons or such an alkyl group having halogen atoms substituted for hydrogen atoms; R² is a hydrogen atom, an alkyl group having 1-50 carbon or such an alkyl group having halogen atoms substituted for hydrogen atoms; and n is an integer 0-3.
 4. The polycarbonate resin composition of claim 1 wherein the polycarbonate is a product of melt polymerization of an aromatic dihydroxy compound with a carbonate diester in the presence of from 10⁻⁸ to 10⁻³ mole of an alkali metal or alkaline-earth metal compound per mole of aromatic dihydroxy compound.
 5. A melt-polymerized polycarbonate resin composition comprising(A) a polycarbonate having a viscosity-average molecular weight ranging from about 12,000 to about 18,000, (B) an α-olefin oligomer and (C) 0.00001 to 0.2 parts by weight per hundred parts by weight of polycarbonate of a boron compound.
 6. A polycarbonate resin composition according to claim 5 wherein said polycarbonate comprises 100 parts by weight per 0.001-5 parts by weight of said α-olefin oligomer.
 7. A process for preparing a polycarbonate resin composition for optical uses comprising(A) a polycarbonate resin, (B) an α-olefin oligomer and (C) from 0.1 to 10 parts per million of an acidic sulfur containing compound having a pK of no more than 3which process comprises melt-polymerizing said polycarbonate resin from an aromatic dihydroxy compound and a carbonate diester in the presence of an alkali metal or an alkaline-earth metal compound.
 8. The composition of claim 3 wherein the sulfur-containing compound is butyl para-toluenesulfonate.
 9. The composition of claim 5 wherein the boron compound is selected from the group consisting of boric acid, trimethyl borate, triethyl borate, tributyl borate, trihexyl borate, triheptyl borate, triphenyl borate, tritolyl borate and trinaphthyl borate.
 10. The composition of claim 9 wherein the boron compound is triphenyl borate.
 11. The composition of claim 1 further comprising 0.00001 to 0.2 parts by weight per hundred parts by weight of polycarbonate of a boron compound.
 12. The composition of claim 11 wherein the boron compound is represented by the general formula

    B(OR.sup.3).sub.n' (OH).sub.3-n'

where R³ is a hydrogen atom, an aliphatic hydrocarbyl group, an alicyclic hydrocarbyl group, or an aromatic hydrocarbyl group, and n' is an integer 1-3.
 13. The composition of claim 12 wherein the boron compound is selected from the group consisting of boric acid, trimethyl borate, triethyl borate, tributyl borate, trihexyl borate, triheptyl borate, triphenyl borate, tritolyl borate and trinaphthyl borate.
 14. The composition of claim 13 wherein the boron compound is triphenyl borate.
 15. The polycarbonate resin compositions of claim 5 wherein the boron compound is represented by the general formula

    B(OR.sup.3).sub.n' (OH).sub.3-n'

where R³ is a hydrogen atom, an aliphatic hydrocarbyl group, an alicyclic hydrocarbyl group, or an aromatic hydrocarbyl group, and n' is an integer 1-3. 